Wetting by liquid sodium and fracture path analysis of sodium induced embrittlement of 304L stainless steel

Bassem Barkia (1, 2, 3) , Thierry Auger (4) , Jean Louis Courouau (5) , Julie Bourgon (2)

1 MSSMat - Laboratoire de mécanique des sols, structures et matériaux
2 ICMPE - Institut de Chimie et des Matériaux Paris-Est
3 LMS - Laboratoire de mécanique des solides
4 PIMM - Laboratoire Procédés et Ingénierie en Mécanique et Matériaux
5 CEA - Commissariat à l'énergie atomique et aux énergies alternatives

The wettability of the 304L steel is an important parameter in Liquid Metal Embrittlement studies. Empirically, it is found to be greatly enhanced by pre-exposure to oxygenated liquid sodium. The corrosion interface formed during exposure to sodium has been analyzed at the nanoscale by transmission electron microscopy using the focused ion beam sampling. A thin layer of sodium chromite (Na xCrO2 with x ≤ 1) is detected at the interface validating wetting on an oxide mechanism for the enhanced wetting after pre-exposure. Fracture micromechanisms and the crack path of liquid sodium-embrittled austenitic steel 304L at 573 K have been investigated down to the nanoscale. High-resolution orientation mapping analyses immediately below the fracture surface show that abundant martensitic transformations (γ → α) and twinning occur during deformation of austenite. The preferential crack path is intergranular along the newly formed γ/γ interfaces. It is concluded that these transformations play a major role in the fracture process.

Domaines: Sciences de l'ingénieur [physics]

Bassem Barkia, Thierry Auger, Jean Louis Courouau, Julie Bourgon. Wetting by liquid sodium and fracture path analysis of sodium induced embrittlement of 304L stainless steel. Journal of Materials Research, 2018, 33 (2), pp.121-129. ⟨10.1557/jmr.2017.435⟩. ⟨hal-02162257⟩