A Comparative Study on Tribocorrosion of Two Ni-Cr Model Alloys in Solution of Boric Acid and Lithium Hydroxide

Abstract : Tribocorrosion of two Ni -Cr model alloys was investigated for different contact pressures in a solution of boric acid and lithium hydroxide at room temperature. The sliding tests were performed with a pin - on - disc tribometer designed to evaluate the synergistic effect between corrosion and wear. The combined corrosion -wear degradation during sliding tests was monitored and evaluated by open circuit potential measurements and electrochemical impedance spectroscopy measurements. The sliding track morphology was investigated by SEM and profilometric measurements after sliding tests. The total material loss generated by the deterioration of the protective oxide layer due to combined chemical / electrochemical and mechanical interactions in the sliding track area was assessed and compared from quantitative and qualitative point of view for these two Ni -Cr model alloys.
Document type :
Journal articles
Complete list of metadatas

https://hal-centralesupelec.archives-ouvertes.fr/hal-01245600
Contributor : Catherine Kruch <>
Submitted on : Thursday, December 17, 2015 - 2:17:24 PM
Last modification on : Wednesday, July 1, 2020 - 4:30:04 PM

Identifiers

  • HAL Id : hal-01245600, version 1

Collections

Citation

Claudiu Ionescu, Pierre Ponthiaux, Marioara Abrudeanu, François Wenger, Florina Constantin. A Comparative Study on Tribocorrosion of Two Ni-Cr Model Alloys in Solution of Boric Acid and Lithium Hydroxide. Revista de Chimie, 2011, 62 (11), pp.1077-1084. ⟨hal-01245600⟩

Share

Metrics

Record views

101