Morphological, optical and photovoltaic characteristics of MoSe2/SiOx/Si heterojunctions

Résumé : This work reports the effect of different processing parameters on the structural and morphological characteristics of MoSe2 layers grown by chemical vapour deposition (cVD), using Moo3 and Se powders as solid precursors. it shows the strong dependence of the size, shape and thickness of the MoSe2 layers on the processing parameters. The morphology of the samples was investigated by field emission scanning electron microscopy (feSeM) and the thickness of the deposited layers was determined by atomic force microscopy (AfM). Raman and photoluminescence (pL) spectroscopies were used to confirm the high quality of the MoSe2 layers. Surface composition was examined by photoelectron spectroscopy (XpS). Moreover, the MoSe2/Siox/Si heterojunctions exhibit diode behaviour, with a rectification ratio of 10, measured at ±2.0 V, which is due to the p-i-n heterojunctions formed at the p-Si/SiOx/MoSe2 interface. A photovoltaic effect was observed with a short circuit current density (Jsc), open circuit voltage (VOC) and efficiency of −0.80 mA/cm2, 1.55 V and 0.5%, respectively. These results provide a guide for the preparation of p-i-n heterojunctions based on few-layer MoSe2 with improved photovoltaic response
Document type :
Journal articles
Complete list of metadatas

Cited literature [41 references]  Display  Hide  Download

https://hal-centralesupelec.archives-ouvertes.fr/hal-02635083
Contributor : James Connolly <>
Submitted on : Wednesday, September 16, 2020 - 11:08:41 AM
Last modification on : Saturday, October 10, 2020 - 3:25:50 AM

File

Silva et al. - 2020 - Morpholo...
Publisher files allowed on an open archive

Identifiers

Citation

J. Silva, C. Almeida Marques, A. Viana, L. Santos, K. Gwozdz, et al.. Morphological, optical and photovoltaic characteristics of MoSe2/SiOx/Si heterojunctions. Scientific Reports, Nature Publishing Group, 2020, 10 (1), ⟨10.1038/s41598-020-58164-7⟩. ⟨hal-02635083⟩

Share

Metrics

Record views

73

Files downloads

29