High Temperature Phase Transition Studies and Dielectric Properties of Sr2SbMnO6

Abstract : Sr2SbMnO6 (SSMO) ceramics were, fabricated using the nanocrystalline powders obtained via molten salt synthesis (MSS) method. High temperature X-ray diffraction studies confirmed the structural phase transition (room temperature tetragonal (I4/mcm) to the cubic phase (Pm-3m)) temperature to be around 736K. The discontinuity in the phase transition indicated its first order nature reflecting the presence of ferroelectric-like distortions in SSMO prepared from MSS which seemed to be unique as it was not observed so far in the case of SSMO prepared using solid-state reaction method. The dielectric behavior of SSMO was studied in the 300-950 K temperature range at high frequencies (MHz range) in order to suppress the of space charge and related effects that dominate at such higher temperatures and mask the real phase transition.
Document type :
Conference papers
Complete list of metadatas

https://hal-centralesupelec.archives-ouvertes.fr/hal-02186460
Contributor : Amandine Lustrement <>
Submitted on : Wednesday, July 17, 2019 - 12:21:51 PM
Last modification on : Wednesday, July 1, 2020 - 4:22:03 PM

Identifiers

Citation

K. R. S. Preethi Meher, P.-E. Janolin, Nicolas Guiblin, Gadige Paramesh, K. B. R. Varma. High Temperature Phase Transition Studies and Dielectric Properties of Sr2SbMnO6. 56th DAE-Solid State Physics Symposium (SSPS), Dec 2011, SRM Univ, Kattankulathur, India. ⟨10.1063/1.4709919⟩. ⟨hal-02186460⟩

Share

Metrics

Record views

56